曲胜++陈春风++陈磊++陈静

摘要：针对燃气轮机润滑油防锈性能较差的问题 使用实验室复配技术研制成功燃气轮机润滑油防锈剂 其原料及配比：石油磺酸钙8%、苯并三氮唑0.5% 、环烷基基础油；配制方法：先后称取基础油、石油磺酸钙、苯并三氮唑加入至调合釜中 设定转速500 r/min 缓慢升温至90 ℃ 恒温2 h。将该防锈剂加入到燃气轮机润滑油进行试验考核 结果表明 能有效改善润滑油的防锈性能 解决燃气轮机使用过程中轴承锈蚀问题。

关键词：燃气轮机；防锈剂；轴承腐蚀；整机考核

中图分类号：TE626.36文献标识码：A

Abstract：In order to improve the rust resistance of gas turbine oil， a rust inhibitor was prepared by compounding with 8% of calcium sulfonate， 0.5% of benzotriazole（BTA）， and naphthenic base oil. The mixture was sequentially added to a blending kettle， and heated slowly to 90 ℃ at a stirring rate of 500 r/min， then the rust inhibitor was gained after stirring for 2 h. The performance of gas turbine oil added the above rust inhibitor was evaluated， the results showed that the new developed product has excellent antirust performance and can prevent the gas turbine from rusting.

Key words：gas turbine； rust inhibitor； axletree corrosion； overall assessment with turbine

0引言

金属材料在生产施工及应用中由于环境的影响产生锈蚀 损失巨大[1] 全世界金属由于被腐蚀、锈蚀造成的损失约占每年所熔炼金属总量的三分之一[2]。

舰船燃气轮机具有功率大、尺寸小、质量轻、起动迅速、加速性和机动性好、寿命长、操作简单、维护方便、工作可靠、润滑油消耗少、功率范围宽等优点 广泛用于航空工业及海洋船舶业中。由于燃气轮机运转停车过程中 系统内温差较大 水汽会在部件表面凝结 气封凝水 渗透进水均造成发动机部件的锈蚀 特别是海洋高温、高湿气候条件 更容易发生锈蚀 主要包括化学腐蚀、微生物腐蚀、电偶腐蚀、空泡腐蚀以及冲刷腐蚀等 化学腐蚀发生在海洋装备的各个部位 微生物腐蚀加快材料腐蚀的速度 电偶腐蚀使异种金属接触中造成其中的一种金属加速腐蚀的现象[3]。这些都会导致燃气轮机运行的安全性降低 发动机使用寿命缩短 造成严重的经济损失[4-5]。……