摘要：为了系统地评估泡沫沥青温拌橡胶沥青混合料的性能，提出合理的生产施工工艺，针对拌和温度与拌和效果的关系、马歇尔击实成型与压实密度的关系以及SHRP旋转压实成型与压实密度的关系展开研究。研究成果包括击实温度、发泡用水量、旋转次数与密度的关系，这些成果可为现场施工工艺的设计及节能效果的评估提供重要的参考数据。

关键词：泡沫沥青；温拌工艺；橡胶沥青；施工工艺

中图分类号：U414.21 文献标志码：B

Abstract： In order to systematically evaluate the performance of rubberized asphalt mixture produced with foaming and warm mix technology， proper production process and construction technology were proposed， and the relationships between the mixing temperature and effect， Marshall compaction shaping and compaction degree， and SHRP gyratory compaction shaping and compaction degree were studied. The correlation between the compaction degree and the compaction temperature， water amount for foaming and the number of rotations was obtained， which provides data basis for on-site construction technology design and energy savings assessment.

Key words： foamed asphalt； warm mix technology； rubberized asphalt； construction technology

0 引 言

近年来，橡胶沥青混合料以其优良的高温稳定性、低温抗裂性、抗水损坏、抗老化和抗疲劳性在国内得到了大范围的应用[1-2]。但是橡胶沥青在生产过程中需将沥青加热到180℃，集料加热到190℃，而高温带来的弊端众所周知。泡沫沥青温拌技术以其节能减排的显著优势得到越来越广泛的应用，许多研究结果表明，泡沫沥青温拌技术能够有效降低沥青混合料的施工操作温度，且泡沫沥青温拌混合料的路用性能仍能达到热拌沥青混合料的标准[3-4]。

本文为了系统地评估泡沫沥青温拌橡胶沥青混合料的生产施工性能，提出生产施工工艺，针对拌和温度与拌和效果的关系、马歇尔击实成型与压实密度的关系、SHRP旋转压实成型与压实密度的关系展开研究。

1 拌和温度研究

1.1 试验方案

本文研究使用的橡胶沥青采用90#基质沥青，掺入20%的30目胶粉，在现场加工而成。采用AR-AC-13橡胶沥青混合料的配合比设计。

（1）室内进行AR-AC-13沥青混合料拌和性能的试验，级配如表1、图1所示。……