过硫磷石膏矿渣水泥混凝土中PSC浆磷石膏含量测定方法研究

林宗寿，吕治江

(武汉理工大学硅酸盐建筑材料国家重点实验室,武汉 430070)

摘要：通过分离过硫磷石膏矿渣水泥混凝土中的过硫磷石膏矿渣水泥浆，并测定各原料的SO3含量，然后根据各原料SO3的平衡关系，计算出了过硫磷石膏矿渣水泥混凝土中的过硫磷石膏矿渣水泥浆的磷石膏含量。经实验反复验证，显示磷石膏含量的测定误差均可在1.0%范围之内，可作为过硫磷石膏矿渣水泥混凝土生产过程中磷石膏配合比的日常控制和测定方法。

关键词：过硫磷石膏矿渣水泥混凝土；磷石膏含量；测定方法

doi:10.3963/j.issn.1674-6066.2015.04.001

Abstract:Through the separation of the Excess-Sulfate Phosphogypsum Slag pulp from the Excess-Sulfate Phosphogypsum Slag Cement Concrete, and the determination of the SO3 content in each material, this study calculated the Phosphogypsum Content in the Excess-Sulfate Phosphogypsum Slag pulp of the Excess-Sulfate Phosphogypsum Slag Cement Concrete according to the equilibrium relationship of SO3 in each material. Through repeated verification, it showed that the measurement deviation of the Phosphogypsum Content is within 1.0% range, so this method can be used to daily control and determine the mix proportion of the Phosphogypsum during the production of the Excess-Sulfate Phosphogypsum Slag Cement Concrete.

收稿日期：2015-06-14.

基金项目：国家高技术研究发展计划(863)项目(2012AA06A112).

作者简介：林宗寿(1957-)，教授．E-mail:13807182067@163.com

Study of the Determination Methods of the PSC Pulp Phosphogypsum

Content in the Excess-sulfate Phosphogypsum Slag Cement Concrete

LINZong-shou，LVZhi-jiang

(The State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology,

Wuhan 430070, China)

Key words:excess-sulfate phosphogypsum slag cement concrete;phosphogypsum content;determination Methods

林宗寿等[1-13]经过多年研究,开发出一种磷石膏基免煅烧水泥,后更名为“过硫磷石膏矿渣水泥”。过硫磷石膏矿渣水泥(PSC)是一种采用40%～50%的磷石膏、40%～50%的矿渣、2%的钢渣和约4%的硅酸盐水泥熟料经混合、粉磨制成的新型水硬性胶凝材料。为进一步节能降耗，林宗寿等[9-13]越过了过硫磷石膏矿渣水泥的生产环节，采用磷石膏浆、矿渣粉、普通硅酸盐水泥、砂、石和外加剂，直接搅拌制成了过硫磷石膏矿渣水泥混凝土(PSCC)，并对过硫磷石膏矿渣水泥混凝土的工艺参数进行了探索。

根据资料[5]可知，PSCC的PSC浆中磷石膏含量大小对其性能有所影响。PSC浆中磷石膏含量过高(超过50%)，会引起PSCC强度大幅度下降；PSC浆中磷石膏含量过低(小于40%)，PSCC的强度将不再明显提高，节能环保效益下降，将失去生产该产品的意义。……