摘要：本研究是以生物质燃气为热处理介质对落叶松板材进行热处理，处理温度为210℃，处理时间为4 h，检测分析落叶松板材热处理后对室外耐久性、物理力学性能及室内抑菌性的影响。结果表明：经过热处理后落叶松板材的室外耐久性和室内抑菌性均有改善，尺寸稳定性提高，除顺纹抗压强度和抗弯弹性模量略有提高，其它力学性能总体呈下降趋势。

关键词：热处理；落叶松板材；耐久性；力学性能

中图分类号：S 781文献标识码：A文章编号：1001-005X（2015）01-0046-03

The Effects of Heat Treatment on Durability

and Mechanical Properties of Larix spp.

Hua Jieqiong，Luo Fasan，Xu Min*

（Key Laboratory of BioBased Material Science and Technology of Ministry of Education，

Northeast Forestry University，Harbin 150040）

Abstract：Larix spp.plates were heated by biomass gas at processing temperature of 210℃ and processing time of 4 hours.The exterior durability，physical and mechanical properties，and antibacterial activity of Larix spp.plates were tested and analyzed.The results showed that the exterior durability，antibacterial activity and dimensional stability of Larix spp.were improved after heat treatment.The compression strength parallel to the grain and bending modulus of elastic（MOE）increased slightly while other mechanical properties decreased.

Keywords： heat treatment；larix spp.plate；durability；mechanical properties

收稿日期：2014-6-12

基金项目：国家林业公益性行业专项（201204709）

第一作者简介：华杰琼，硕士研究生。研究方向：木材热处理。

*通讯作者：许民，教授，博士生导师。研究方向：木材保护、生物质复合材料。

引文格式：华杰琼，罗法三，许民.热处理对落叶松板材耐久性及力学性能的影响[J].森林工程，2015，31（1）：46-48.木材高温热处理是指在保护性气体环境或液体介质中，对木材进行短期热解处理（温度160～250℃）的一种木材物理保护技术[1]。采用热处理技术能够有效提高木材的尺寸稳定性和耐腐性能，大幅度提高低质木材的产品附加值，实现了低质木材的高效利用。

热处理主要采用氮气、二氧化碳等做保护气体，存在的主要问题是处理成本高，热处理时从木材中蒸馏出来的物质含有酚类、焦油等气体，对环境造成污染。本研究采用的生物质燃气主要来源于木质废弃物，以此作为热源和加热介质对木材进行热处理，与其它热处理介质（如植物油等）相比，具有处理成本低、燃料来源广泛、绿色环保等特点。……