师晖军

摘要：为制备高性能二灰稳定碎石混合料，采用体积法对不同类型的二灰稳定碎石混合料进行了配合比设计，并通过无侧限抗压强度试验和劈裂强度试验对其进行了路用性能研究。结果表明：激活剂的加入使得二灰稳定碎石混合料的抗压强度、劈裂强度和抗压回弹模量均有大幅度的增长，并且能提高其抗冲刷性能，但抗温缩性能略有降低。

关键词：二灰稳定碎石；混合料设计；激活剂；路用性能

中图分类号：U414.03文献标志码：B

Abstract： In order to prepare high performance lime flyash stabilized aggregate， different types of mixtures were designed with volume method， and pavement performance including strength， stiffness， antishrinkage and antierosion properties were studied. The results show that compressive strength， splitting tensile strength and compressive modulus of lime flyash stabilized aggregate can be greatly increased by adding activator. Lime flyash stabilized aggregate with activator has better antierosion properties than the conventional one. And activator has little effect on antidry shrinkage properties of lime flyash stabilized aggregate， but it can decrease slightly the antitemperature shrinkage performance.

Key words： lime flyash stabilized aggregate； mixture design； activator； pavement performance

0引言

二灰稳定碎石具有较高的强度和板体性能以及比其他基层材料更好的抗裂性能，应用二灰稳定碎石可以变废为宝，不仅能减少工业废渣对环境的危害，而且可以降低工程造价，因此已被普遍应用于高等级公路基层的修筑[15]。但研究与实践证明，与水泥稳定碎石相比，二灰稳定碎石的早期强度较低。为了提高其早期强度，在以往的工程实践中曾采用添加碱的方法，但终因造价过高或施工工艺太复杂而未获成功。另一方面，低活性粉煤灰在公路中的应用受到一定的限制，因此必须对二灰稳定碎石的性能进行改善，以满足公路基层施工的技术要求[67]。

1原材料性质

1.1石灰

石灰采用西安市售普通石灰，检测其技术指标如表1所示，符合《公路路面基层施工技术规范》（JTJ 034—2000）[8]中对石灰性质规定的三级生石灰或三级消石灰技术要求。

1.2粉煤灰

粉煤灰采用重庆产的一种低钙粉煤灰，其检测结果如表2所示，其中……