柴文国

摘要：填充墙抹灰裂缝已成为高层建筑通病，很难杜绝，为提高邯钢百二生活区1#住宅楼工程抹灰的质量及外观效果，促使本工程达到“省优工程”，我单位领导高度重视，派我单位技术主干及长期从事民用建筑的老工程师，结合我单位多年的施工经验及本工程实际情况，对填充墙抹灰裂缝产生的原因进行科学的分析，制定相应的方案。

关键词：加气混凝土砌块填充墙抹灰裂缝原因措施

Abstract: filling wall plastering has become a common cracks high-rise building, it is difficult to put an end to, in order to improve the hangang 102 living area of residential building project of the 1 # plastering quality and exterior effect, make the project to "provincial fine-quality project", I unit the leadership, more attention sent me unit technology backbone and engaged in civil building of old engineer, combined with my unit years of construction experience and the actual project, fill walls of external thermal insulation cracking reason for scientific analysis, formulating a plan.

Keywords: aerated concrete block filling wall plastering crack causes measures

中图分类号：TU37 文献标识码：A 文章编号

前言

我们的方案主要针对剪力墙结构，加气混凝土砌块填充墙墙面抹灰裂缝现象，系统的分析填充墙出现裂缝的原因，并提出在砌筑加气块时、后期抹灰时采取的对填充墙裂缝产生所采用的必要、有效的预控措施。

一、 编制依据

1、 施工设计图纸

2、 《邯钢百百家村生活区旧城改造1#住宅楼施工组织设计》

3、 《砌体工程施工质量验收规范》GB50203-2002

4、 《建筑装饰装修工程质量验收规范》GB5021-2001

5、 《建筑室内抹灰施工工艺标准》

二、 工程概况

邯钢百二生活区1#住宅楼位于邯钢百二生活区内，地上十八层地下二层，剪力墙结构，标准层层高2.8m，主体内部填充墙采用加气混凝土块砌筑，在后砌墙位置每隔两皮砖，安装2根Φ6的一级钢筋，钢筋采用后植法，平锚墙内长度为12cm，每道墙三道钢筋，中间一道钢筋为通常钢筋，后砌墙下部砌筑五层小砖，墙体抹灰卫生间及厨房为防水砂浆，交工时要求为毛面，已有利于房主自行进行二次装修，其余地方均粉刷石膏。……