新型受阻酚类抗氧剂的合成与性能研究

李翠勤1,王 俊1,方 宏2,葛腾杰2

(1.东北石油大学化学化工学院,黑龙江大庆163318;2.大庆化工研究中心,黑龙江大庆163712)

以2,6-二叔丁基苯酚原料,合成了1种新型受阻酚抗氧剂2,6-二叔丁基-4-氨基苯酚,研究了该新型抗氧剂对聚烯烃材料的抗氧化作用。结果表明,以锌粉为还原剂,8.5%氯化钙水溶液用量为90 mL,溶剂乙醇用量为100 mL,在80℃下反应8 h,新型受阻酚抗氧剂的产率达80%以上,熔程为112.2～113.3℃。该抗氧剂在2种聚烯烃材料中均具有良好的加工稳定性和抗氧化性能,氧化诱导期与市售抗氧剂1076相当,优于抗氧剂BHT;经5次挤出后,添加新型抗氧剂的聚烯烃材料的熔体流动速率变化很小,但拉伸强度和断裂伸长率大幅度提高。

2,6-二叔丁基苯酚;2,6-二叔丁基-4-氨基苯酚;受阻酚抗氧剂;氧化诱导期;抗氧化性能

Abstract:A novel hinderd phenolic antioxidant 2,6-di-tert-butyl-4-aminophenol was synthesized with 2,6-di-tert-butylphenol as a raw material.When zinc powder was used as a reducing agent,ethanol as a solvent was 100 mL,the amount of calcium chloride solution was 90 mL,the reaction temperature was 80℃and the reaction time was 8 h,the yield of the product reached 80%and its melting point was between 112.2℃and 113.3℃.When loaded in polyolefin resins,the antioxidation property of the novel one was equal to antioxidant 1076 and was superior to antioxidant BHT.After extrusion of 5 times,the melt flow rate of the two polyolefins containing the novel antioxidant changed a little,and the tensile strength and the elongation at break increased.

Key words:2,6-di-tert-butylphenol;2,6-di-tert-butyl-4-aminophenol;hinderd phenolic antioxidant;oxidation induction time;oxidation resistance property

0 前言

自1937年世界上第一个具有受阻酚结构的抗氧剂BHT问世以来,受阻酚类抗氧剂的开发和研究倍受关注[1]。受阻酚类抗氧剂具有抗氧效果好、热稳定性高、对制品无污染、不着色、与制品相容性好等优点,成为目前应用最广泛、用量最大的主抗氧剂[2-3]。随着高分子工业的发展,对抗氧剂的要求不断提高。因此开发具有结构新颖、性能优良的新型受阻酚类抗氧剂,成为抗氧剂开发的主流和趋势。目前,许多助剂公司在注重对传统产品进行工艺改进和性能改良的同时,还致力于新产品、新结构的研究,相继开发许多性能-效益平衡性较好的新型受阻酚类抗氧剂,如抗氧剂Mark AO-80、Irganox1425、超支化抗氧剂[4-5]。……