荆 鹏，刘 峰，王晓蕾，黄 玮，丛玉凤

（辽宁石油化工大学 环境与生物工程学院，辽宁 抚顺 113001）

环保型热熔压敏胶的制备*

荆 鹏，刘 峰，王晓蕾，黄 玮*，丛玉凤

（辽宁石油化工大学 环境与生物工程学院，辽宁 抚顺 113001）

实验采用加氢改性后的C5石油树脂，即氢化C5石油树脂作为热熔压敏胶(HMPSA)配方中的增黏剂，SBS热塑性弹性体为增韧剂，同时还加入了增塑剂和少量的抗氧剂和防老剂等助剂，来制备环保型热熔压敏胶。并通过对压敏胶产品初黏性、180℃熔融黏度、剥离强度等性能的测定，得到了一个最佳的热熔压敏胶配方。实验结果表明，当氢化C5石油树脂的质量分数为40%，增塑剂为35%，SBS为20%，抗氧剂和防老剂等助剂为5%时，环保型热熔压敏胶的性能达到了行业标准。

热熔压敏胶；氢化C5石油树脂；初黏性；剥离强度

Abstract:The environment-friendly hot-melt pressure-sensitive adhesive(HMPSA)was prepared,with using hydrogenated C5petroleum resin as a tackifier,SBS thermoplastic elastomer as the toughener,and adding plasticizer and a small amount of antioxidant.By testing the initial adhesion,180℃melt viscosity and peeling strength of the product,a optimal formula for hot-melt pressure-sensitive adhesive was obtained.The results showed that the best formula was as follows:hydrogenated C5petroleum resin accounts for 40% (mass percentage,the same below),plasticizer 35%,SBS thermoplastic elastomer 20%,antioxidant 3%and anti-aging agent 2%.The products could meet the industrial standards.

Key words:Hot melt pressure sensitive adhesive;hydrogenated C5petroleum resin;initial adhesion;peeling strength

前 言

随着现代经济飞速发展，人们生活质量正在不断提高，对生活用品的需求也在不断提升，除了对于产品性能的要求，安全和环保的理念也已经深入人心。热熔压敏胶[1]具有热熔及压敏双重性能，在熔融状态下涂布，冷却后施加轻压即可快速粘合。由于热熔压敏胶不含有机溶剂，不污染环境，而且制造简单，使用方便，用途[2]广泛，因此是今后压敏胶的发展方向。C5石油树脂[3]以其性能优良、安全、环保等多方面优势，近些年来备受人们的青睐，其作为一种低相对分子质量、热塑性树脂，具有降凝、增黏[4]和改善黏度的性能[5]，可做为SBS热熔型压敏胶配方中的增黏剂，起到提高胶体初黏性，改善胶体润湿性等作用。……