摘要：对深地深海油气勘探用测井电缆铠装钢丝进行了研发试制，试制结果表明：铠装钢的盘条微观结构为全片层的珠光体组织，未出现先共析铁素体、先共析渗碳体和马氏体等异常组织，轧制后的冷却工艺合理，抗强度为1 623 MPa。盘条冷拉拔为钢丝后，珠光体中的片层渗碳体出现扭转、断裂的现象，出现了颗粒状渗碳体的形貌，冷拉拔加工硬化使钢丝抗拉强度提升至2 084 MPa。

关键词：深地深海;承荷探测电缆;铠装钢;微观组织

Abstract： The development and trial production of armored steel wire for logging cable used in deep-sea oil and gas exploration are carried out. The results show that the microstructure of armored steel wire rod is full lamellar pearlite structure， and there are no abnormal structures such as proeutectoid ferrite， proeutectoid cementite and martensite. The cooling process after rolling is reasonable， and the strength is 1 623 MPa. After the wire rod is cold drawn to steel wire， the lamellar cementite in pearlite appears torsion and fracture， and the morphology of granular cementite appears. The tensile strength of steel wire is increased to 2 084 MPa by cold drawing hardening.

Key words： deep-land and deep-sea; load bearing detection cable; armored steel; microstructure

随着石油天然气的日益消耗，为了获得更多的油气资源，深地深海油气田的勘探工作需要使用到大量的高强度的承荷探测电缆[1]。经常使用在环境恶劣的深地深海领域，其长度可达万米，随着深度的不断增加，温度、压力以及自身重力等复合外界条件势必会对电缆的安全工作产生影响[2]。附加海底地震，海洋暗流的冲涮以及大量海底生物的撞击等因素，要求深地深海探测电缆必须具有较高的使用性能，但是铠装电缆的外壳通常为橡胶，其制备工艺简单，强度不足以及无法承受高温、高压等工作环境，无法满足深地深海油气勘探的使用要求[3-5]。因此我国早在1 977年就开始了承荷电缆使用铠装钢丝的研发，铠装钢丝的抗拉强度逐步提高，抗拉强度逐步直到2 000MPa甚至更高[6-8]。江苏华能电缆股份有限公司自主研发了抗拉强度为2 000 MPa、直径为Φ1.7 mm的深地深海用特种电缆铠装钢丝。

1实验材料及方法

实验材料采用电炉進行冶炼，完成后浇铸为钢锭，钢锭重新升温后采用锻压机锻打为50 × 50 × 1000 mm3的钢棒，在钢棒上取样化验化学成分，结果如表1所示。……