龙晶 沈兰萍

摘 要：为了改善纯棉织物导湿速干性差、吸湿后衣服与皮肤严重的黏着性等问题，以Coolmax纱线和防紫外竹/棉混纺纱线为原料，设计开发4种不同组织结构的防紫外吸湿速干织物，测试4种不同组织结构织物的基本服用性能、吸湿速干性能和防紫外性能。结果表明：这4种组织织物均具有较好的防紫外吸湿速干性能。其中，缎纹组织为综合性能最佳的织物组织。

关键词：Coolmax纱线;混纺纱;防紫外;吸湿速干;组织结构

中图分类号：TS102.5

文献标志码：A

文章编号：1009-265X（2021）02-0039-04

Abstract：In order to address the defects of poor wet permeability and quick drying， and wetted clothes clinging to skin， anti-ultraviolet， moisture-absorption and quick-drying fabrics of four different weave structures were designed and developed using Coolmax yarns and anti-ultraviolet bamboo/cotton blended yarns as raw materials. The fabrics were tested for the basic wearability， wet permeability， quick-drying and ultraviolet protection. The results show that the fabrics of the four weave textures all are of good ultraviolet protection， wet permeability， and quick-drying performance. Among the four structures， satin weave performs best in respect of overall performance.

Key words：Coolmax yarns; blended yarns; anti-ultraviolet; moisture absorption and quick-drying; weave structure

作者简介：龙 晶（1995-），女，陕西渭南人，硕士研究生，主要从事纺织材料与纺织品设计方面的研究。

近年来，温室效应的加剧，使人们对面料的抗紫外线和吸湿快干性要求越来越高[1-2]。目前，市场上出现的防紫外纺织品大多数都是通过后整理的方式实现的，但这种方式存在很多缺陷，如耐久性差、舒适性差等问题[3]。此外，对于吸湿速干织物的研究只集中在吸湿导湿纤维[4]和单一功能织物上，且在针织领域研究诸多，周亚利等[6]设计并开发了吸湿快干抗菌复合针织弹力牛仔面料;李伟涛[7]采用了云母冰凉纤维，开发轻薄的云母冰凉纤维针织物;朱碧红、葛俊伟等[8-9]对织物吸湿排汗性、刚柔性、起毛起球性等服用性能及物理性能进行了测试，分析了织物组织结构对针织物综合性能的影响。而对兼具防紫外线、除臭、透气、抑菌等多功能的吸湿速干机织物的研究还处于空白状态。市场上常见的吸湿性产品主要以棉、黏胶等具有优良吸湿性的织物为主[10-11]，但当人们在剧烈运动时，该类织物不能及时的将汗液导出，使衣服与人体处于黏贴状态，极大地影响织物的舒适性[12]。……