黄春晖 张喆 钱若霖

摘 要：针对建筑物在施工和拆除过程中产生大量建筑垃圾带来的资源短缺和环境污染问题，尝试将混凝土和废砖制备成再生骨料，进而完成对混凝土和砖石的回收。为改善再生骨料的力学性能，利用质量浓度为2%的纳米硅溶胶溶液对骨料进行改性。在此基础上，掺入一定量的PVA纤维，并研究了纤维纳米再生混凝土的基本力学性能。结果表明，加入纤维后，纳米再生混凝土压缩性能有所降低，但使劈裂拉伸性能和弯曲性能分别比基准混凝土增加了10.8%和8.35%，证实了PVA纤维对再生混凝土有优化作用。

关键词：再生骨料;力学性能;聚乙烯醇纤维;再生混凝土

中图分类号：U416.1 文献标识码：A 文章编号：1001-5922（2021）08-0080-04

Application of Construction Waste Recycling Material in Subgrade Construction

Huang Chunhui， Zhang Zhe， Qian Ruolin

（Shaanxi Polytechnic Institute， Xianyang 712000， China）

Abstract：In view of the shortage of resources and environmental pollution caused by a large amount of construction waste in the process of construction and demolition of buildings， this paper attempts to prepare recycled aggregate from concrete and waste brick， and then complete the recycling of concrete and masonry. In order to improve the mechanical properties of recycled aggregate， nano silica sol solution with mass concentration of 2% was used to modify the aggregate. On this basis， the basic mechanical properties of fiber nano recycled concrete are studied by adding a certain amount of PVA fiber. The results show that after adding fibers， the compressive properties of nano recycled concrete are decreased， but the splitting tensile properties and flexural properties are increased by 10.8% and 8.35% respectively compared with the reference concrete， which proves that PVA fiber has the optimization effect on recycled concrete.

Key words：recycled aggregate; mechanical properties; polyvinyl alcohol fiber; recycled concrete

隨着建筑行业的发展，每年产生的建筑垃圾成倍增加。据不完全统计，部分城市一年产生的建筑垃圾占该城市垃圾总量的35%～40%。因此，如何回收利用这些建筑垃圾，是目前较为重要的问题。为更好利用再生混凝土，宫宝汝（2019）提出将废弃混凝土再生骨料用于铁路基床[2];张全贵（2020）则研究了利用再生骨料配制透水混凝土的一些关键点[4]。但再生骨料来源于建筑垃圾，具有很多先天损伤，造成制备的混凝土力学性能差的现象，不适用于地基工程。由此，本研究尝试用纳米硅对再生骨料进行改性，修复先天损伤，并在此基础上，掺入一定量的聚乙烯醇纤维，以求制备出一种适用于路基施工的再生骨料混凝土。

1 材料与方法

1.1 材料与设备

本试验所用材料与设备如表1、表2所示。……