高山雪 邢梦雨 吴宇佳 徐一卢 陈蕾

摘要：塑料制品在环境中老化后，表面特征也会发生变化，并对其生物毒性产生很大的影响。本文采用傅立叶变换红外光谱的表征方法，对比老化前后塑料农膜的红外吸收光谱，研究塑料农膜老化过程中表面官能团的变化特征。研究发现塑料农膜表面在老化过程中发生氧化，并吸附了农药等物质，增加了塑料农膜的生态风险。

关键词：塑料农膜;老化;红外光谱;生态风险

Abstract：The surface feature of plastic products will change during the aging process in the environment，which will have great impact on the biological toxicity. This paper studied the changes in surface feature of plastic film during aging process by comparing the infrared absorption spectrum of the plastic films before and after aging using fourier transforms infrared spectroscopy.Our results indicated that oxidation took place on the surface of the film during the aging process and pesticides might be adsorbed，which might increase the ecological risk of plastic film.

Key words：Plastic film;Ageing;Infrared spectroscopy;Ecological risk

塑料農膜在农业生产中被广泛使用，自然的风力、雨淋与阳光辐射会使塑料农膜发生老化，甚至碎裂成粒径小于5 mm的微塑料。微塑料在环境中持久存在，不仅会抑制植物生长、改变相关微生物酶活性并增加生物死亡率，还可在生物体内累积，通过食物链威胁到人类的健康。研究表明，老化的微塑料往往更容易在生物体内积累，并产生更高的生物毒性，这可能与塑料老化过程中表面官能团的变化有关。因此本文采用傅立叶变换红外光谱的表征方法，研究塑料农膜老化过程中表面官能团的变化特征。

1 材料与方法

1.1 仪器与试剂

傅立叶变换红外光谱仪（型号IR-360，购自美国Nicolet公司）;过氧化氢（分析纯，购自上海瓦兰生物科技有限公司）、饱和氯化钠溶液（1.2 g/cm3）、95%乙醇溶液、氯化亚铁（分析纯，购自上海展云化工有限公司）、超纯水等。

1.2 实验方法

1.2.1 样品的采集与处理

采集的样品来自南通市如东县农业生产大棚上使用过的老化农膜，对照样品是从当地商店购买的未使用过的塑料农膜。……