和蕊 李鹏 孙俊伟

摘 要：采用缓慢滴碱法制备聚合氯化铝，氢氧根离子浓度和温度是影响Al2O3含量的主要因素，初始铝浓度和氢氧根离子浓度是影响盐基的主要因素.最佳制备条件为：初始铝浓度0.3 mol/L，OH-浓度0.5 mol/L，加热温度70℃，搅拌强度300 r/min，溶液穩定时间24 h.盐基度为70%的聚合氯化铝具有较好的混凝性能，沉后水浊度随投加量的增加回升较为缓慢，混凝过程中生产絮体粒径较为粗大，有利于静沉.

关键词：盐基度，混凝，聚合氯化铝

[中图分类号]O69   [文献标志码]A

Abstract：In the preparation of polyaluminium chloride by slow dropping alkali method，the concentration and temperature of hydroxide ion are the main factors affecting the content of Al2O3，and the initial concentration of aluminium and hydroxide ion are the main factors affecting the base.The optimum preparation conditions are including： initial aluminum concentration 0.3 mol/L，OH- concentration 0.5 mol/L，heating temperature 70℃，stirring intensity 300 R/min，solution stabilization time 24 h.The polyaluminium chloride with base degree of 70% has better coagulation performance，the turbidity of water after sedimentation rises slowly with the increase of dosage，and the floc particle size produced in the coagulation process is relatively large，which is conducive to static sedimentation.

Key words：basicity;polyaluminium chloride;coagulation

净水厂在混凝阶段主要依赖投加聚合氯化铝控制浊度指标.生产中投用的聚合氯化铝盐基度范围较宽，不同温度下进水时，聚合氯化偶尔会表现出混凝性能欠佳的情况.[1-3] 混凝性能受很多因素的影响，进水水质的水温是影响因素之一.为了解决水温变化给水厂带来的问题，笔者研究不同盐基度对不同水温水质的影响，优选出不同温度下具有较好混凝效果盐基度的最佳混凝剂，用以指导生产.

1 材料与方法

1.1 实验材料

试验水质 南方冬夏温差较大，冬季水厂进水水温分布在7～10℃，秋季7～12℃，春季9～14℃，夏季20～25℃.现场取样，原水浊度一般为1.5～2.5 NTU，耗氧量低于2 mg/L，氨氮0.08 mg/L左右.

主要仪器 浊度仪（无锡市光明浊度仪厂，STZ-A1），JTY混凝试验搅拌仪（武汉市梅宇仪器有限公司，MY3000-6B），静态激光光散射仪（上海魁元科学仪器有限公司，BI-200SM）.

1.2 实验方法

聚合氯化铝的制备 将三口烧瓶置于恒温水浴锅内，调节水浴锅温度至目标温度后，加入一定体积的初始铝溶液，打开……