摘 要：采用高分离性能NaA分子筛膜对医药企业对回收乙醇1及回收乙醇2进行脱水精制回收，并對其渗透汽化性能进行测试，在操作温度为85℃、真空度为300～500Pa的条件下，对乙醇含量为90wt.%的乙醇/水体系进行分离，随着时间的进行渗透通量平均在1.1kg·m-2·h-1，渗透液中平均水含量99.6wt.%。运行结果表明，该两种原料通过NaA分子筛膜进行乙醇精制回收可行且效果较好。通过运用该膜工艺医药企业建立10000t/a乙醇脱水制备精制回收乙醇，运行以来将含水量10%的回收乙醇1和回收乙醇2脱水至含水量在0.5%以下，连续运行稳定分离结果较好，节能减少成本效果显著。

关键词：NaA分子筛膜;乙醇脱水;渗透汽化

Abstract：high performance NaA zeolite membrane was prepared by hydrothermal synthesis method， and its pervaporation performance was tested. Under the condition of operating temperature of 75℃ and vacuum degree of 300-500 Pa， the ethanol/water system with ethanol content of 95 wt.% was separated. The permeation flux was more than 2.0 kg·m-2·h-1 and the separation coefficient was more than 9000. The characterization and test results show that the prepared NaA zeolite membrane has high crystallinity， continuous density and high repeatability. The crude ethanol with water content of 10% has been dehydrated to less than 0.05% since its operation in the 50000 t/a ethanol dehydration enterprise. The continuous operation and stable separation results are good.

Keywords：NAA molecular sieve membrane;ethanol dehydration;pervaporation

0 前言

无水乙醇是一种重要的基本化工原料和溶剂，有着广泛的用途，在油漆、染料、制药、化妆品、橡胶、电子工业等领域应用广泛。乙醇在使用过程中与水易形成共沸体系，导致乙醇的回收利用较为困难，传统的共沸精馏脱水技术会引入新的杂质，且过程能耗大，环境污染严重，亟待需要节能、高效的乙醇脱水工艺。

分子筛膜是一种新型无机膜，它具有耐高温、抗化学与生物侵蚀、通量大、分离选择性高等优点，在许多渗透汽化/蒸汽渗透过程中展示出优异的应用前景。渗透汽化是在混合物（液态或气态）中某组分蒸气压差推动下，利用组分通过膜的吸附（溶解）与扩散速率的不同来实现分离的过程。NaA分子筛膜技术作为一种新型的膜分离技术，具有一次分离度高、操作简单、无污染、低能 耗的特点，解决乙醇提纯过程的高能耗问题。……