桉木单板/聚氯乙烯膜复合材料的制备工艺1)

王丹丹曹阳王翠翠韦文榜张双保

(木材科学与工程北京市重点实验室(北京林业大学)，北京，100083)

以人工林速生材桉木为基材，聚氯乙烯膜代替传统胶黏剂制备木塑复合材料，解决了甲醛释放、白色污染等问题。采用热压—冷压工艺，以热压温度、时间及塑料添加量3个因素为自变量，胶合强度为响应值，通过响应面分析确定了最优生产工艺；并采用扫描电子显微镜观察其界面形态，即热压温度为183 ℃，热压时间为452 s，塑料添加量为320 g/m2。试验表明：桉木单板/聚氯乙烯膜制备木塑复合材料工艺具有可行性，其胶合强度达1.14 MPa，满足GB/T 9846—2015标准中Ⅱ类胶合板的要求。

桉木；聚氯乙烯膜；木塑复合材料；胶合强度；响应面法

To solving pollution problems such as formaldehyde and white pollution, we used the fast-growing eucalyptus wood as based material and Polyvinyl chloride film which insteaded traditional adhesive to make wood-plastic composites materials by hot-cold pressing crafts. Hot-pressing temperature, time and the amount of plastics as the independent variable, bonding strength as the response value, we used response surface methodology to optimize the best processing factor, and analyzed the fractural surfaces of samples by a scanning electronic microscope. The best processing factor was hot-pressing temperature of 183 ℃, hot-pressing time of 452 s and PVC films of 320 g/m2. Therefore, it is feasible to make wood-plastic composites by using eucalyptus wood and PVC film. The plywood bonding strength reached 1.14 MPa, which met the requirement of Type Ⅱplywood according to the National Standard of GB/T9846-2015.

桉树作为一种优质速生丰产树种，已成为全球人工林最重要的造林树种之一，有效解决了当前木材短缺的问题。但由于桉树本身生长特性存在一些缺陷，木材强度低，因此加大对桉树高附加值的利用成为当今木材加工行业的重要课题。

以传统的三醛胶制备的人造板产品在使用过程中会不断释放游离甲醛，不仅污染环境，而且还危害人体健康。因此需要寻求可以取代三醛胶的无醛板材胶黏剂。研究表明：塑料可以替代木材传统胶黏剂制备环保型胶合板[1]。大量的塑料制品给生活带来便利的同时也给环境造成了“白色污染”。……