贺欣 班久庆

摘 要：根據海水离子组成，配制了矿化度为50 000 mg/L的人造海水，并围绕Halfaya油田注水系统的环节，确定腐蚀实验试样挂片，通过高温高压动态腐蚀仪对挂片进行腐蚀试验，观察记录实验现象，取垢样对其进行定性分析，总结垢样组成，得出了垢样不含碳酸盐垢、氧化铁垢、硫酸盐垢、硅酸盐垢的结论。

关 键 词：结垢；人造海水；高温高压动态腐蚀仪；定性分析

中图分类号：TE 357 文献标识码： A 文章编号： 1671-0460（2016）08-1797-03

Abstract： Based on composition of seawater ions， artificial seawater with the salinity of 50 000 mg/L was formulated. Aiming at the water injection system in Halfaya oil field， the corrosion test specimens were determined， corrosion test of hanging pieces was carried out by high temperature and high pressure dynamic corrosion tester， the experimental phenomena were observed and recorded， qualitative analysis of scale samples was carried out， the scale composition was summarized. The results show that the scale does not contain carbonate scale， iron oxide scale， sulfate scale and silicate scale.

Key words： scale； artificial sea water； high temperature and high pressure dynamic corrosion tester； qualitative analysis

油层注水是保持地层压力获得较高采收率的一种有效方法，海水则是一种满意的注入液。已有试验证明，注海水比注一般水驱油效率要高5%左右[1]。但是注海水对金属设备和管道会产生腐蚀，结垢与腐蚀往往相互促进，给油气生产造成巨大的经济损失[2]。

油田防腐问题主要是油水井的腐蚀以及输油水管道的腐蚀，是金属腐蚀问题。引起腐蚀的因素之一就是：矿化度高。实验表明当矿化度在12 000～

20 000 mg/L时，水质腐蚀性呈中度，大于20 000 mg/L时水质腐蚀性呈重度，井液的高矿化度是造成腐蚀的因素之一[3]。当矿化度含量增加时，采出水中带电离子浓度增高，金属腐烛速度亦加快[4]。

1 实验内容

（1）模拟海水配制：根据提供的海水离子组成，进行人造海水的配制。

（2）采取被清洗设备的污垢样品，进行成分的定性和定量分析，通常以定性分析为多。垢样分析是确定清洗液配方的首工作，其分析结果能提供污垢的主要成分，是确定清洗剂选择范围的主要依据[5]。

2 实验步骤

2.1 模拟海水矿化度的确定