摘要：本文以T110 D/84 f/12海岛纱×T140 D/136 f DTY（Cupron）铜离子纱为原料，设计开发出具有柔软舒适、抗菌、透气、吸湿排汗等功能的凹凸立体效果鞋面针织面料，探讨了其织造与染色工艺，并详细介绍了关键工艺要点，对今后多样化鞋面针织面料开发有一定的借鉴意义。

关键词：Cupron；鞋面针织面料；织造与染色；抗菌

中图分类号：T184 文献标志码：B

Development of Cupron Antibacterial Knitted Fabric for Shoe Upper

Abstract： Using T110 D/84 f/12 island-in-the-sea yarn × T140 D/136 f DTY copper ion yarn （Cupron） as raw material， a knitted fabric with three-dimensional texture effect as well as soft and comfortable， breathable， antibacterial， moisture absorption and other functions， which can be used for shoe upper， was designed and developed. The knitting and dyeing processes and the key technologies for making this fabric were discussed. This may provide certain reference to the development of diversified shoe upper knitted fabric in the future.

Key words： Cupron； knitted fabric for shoe upper； knitting and dyeing； antibacterial

人在行走、跑步等运动时，脚部会产生较大热量导致出汗，使细菌繁衍滋生，伴随产生大量有害细菌。因此，研究开发新型实用的透气抗菌鞋材面料，成为研究工作者必选的课题。

Cupron纤维是美国卡普诺公司开发的一种新型抗菌纤维，属于一种铜离子纱。主要通过在涤纶或尼龙等纤维内部加入铜离子成分，即在熔融纺丝过程中，把氧化铜粉末分散在熔体中，得到含有氧化铜颗粒的纤维。这种纤维具有良好的抗菌、抗病毒功能。

1 编织工艺

1.1 原材料

抗菌鞋面针织面料产品的原材料采用T110 D/84 f/12海岛纱×T140 D/136 f DTY（Cupron）铜离子纱。

1.2 机台设备

机型：德国卡尔迈耶双面圆机；

机号：24针/25.4 mm；

筒径：864 mm（34″）；

路数：72 F。

1.3 织造工艺

1.3.1 织针排列（图 1）

1.3.2 三角排列

12路一个循环，上机三角排列如表 1 所示，其中∨、∧为成圈三角，∏为集圈三角，—为浮线三角。

1.3.3 织物上机编织（图 2）

1.3.4 穿纱方式

1、3、5、7、9、11路穿纱为T110 D/84 f/12海岛纱；2、4、6、8、10、12路穿纱为T140 D/136 f DTY（Cupron）铜离子纱。

1.4 织物风格

T110 D/84 f/12海岛纱是（T80 D/72 f/12 DTY+T30 D/12 f FDY）包芯复合纱的简称，减量后具有稳定性强，形成织物具有不易变形的特点。其中T80 D/72 f/12 DTY含有864条细纤维，减量开纤后，织物有一种麂皮的手感，与Cupron铜离子纱交织形成凹凸感强的网眼风格。

2 染整工艺