微波烧结WC-Co硬质合金致密化与晶粒生长

娄 静1，易健宏1,2，周承商1

(1. 中南大学 粉末冶金国家重点实验室，长沙 410083；2. 昆明理工大学 材料科学与工程学院，昆明 650093)

分别采用微波烧结和常规烧结制备WC-8Co硬质合金，通过1 000～1 400 ℃温度范围烧结以及1 400 ℃保温0～240 min的微波和常规烧结实验，测量各样品的收缩率、密度和晶粒尺寸，分析其致密化行为和晶粒生长，研究烧结温度和保温时间对合金致密化和晶粒生长的影响。结果表明，与常规烧结比较，微波烧结促进YG8硬质合金的致密化，且获得的合金组织均匀，晶粒细小。另外，保温时间对微波烧结YG8硬质合金的晶粒生长几乎没有影响。

微波烧结；YG8硬质合金；致密化；晶粒生长

Abstract:Microwave and conventional technology were used to sintering WC-8Co cemented carbide. In order to research the effects of temperature and holding time on the densification and grain growth of the alloys, experiments with the temperature in range of 1 000−1 400 ℃, and the holding time in range of 0−240 min at 1 400 ℃ were conducted.The shrinkage, density and grain size of samples were systematically measured to analysis the densification behavior and the grain growth. The result shows that, in contrast to conventional sintering, microwave sintering enhances the densification behavior of WC-8Co alloys, and promotes homogeneous microstructure and finer grains. In addition, no evident influence of holding time on the grain growth of alloys sintered by microwave processing is observed.

Key words:microwave sintering; YG8 cemented carbide; densification; grain growth

硬质合金是一种以难熔金属化合物(WC、TiC、Cr2C3等)为基体，以过渡金属(Co、Ni、Fe等)或合金作粘结剂，采用粉末冶金方法制备的一种材料。由于具有高弹性模量、高硬度和强度、良好的热稳定性和优异的耐磨性，且抗冲击性、耐腐蚀性、导热导电性、红硬性均较好，硬质合金自问世以来一直备受关注，在切削加工、凿岩采掘、成形模具、耐磨零件等方面得到了广泛应用[1]。随着金属加工业、电子工业、医疗以及城市建设的迅速发展，世界范围内对高性能硬质合金材料的需求日益扩大，如集成电路板的微型钻头、用于印刷电路板引线切头的圆片切刀等材料，且对强度、韧性、刚度(弹性模量)等性能均提出严格要求[2]。……