酯型无灰分散剂的合成研究

王辉，孙翔兰，刘功德

(中国石油大连润滑油研究开发中心，辽宁大连116032)

以烯酐、新戊基多元醇为原料，通过酯化反应合成酯型无灰分散剂，研究了酯型分散剂的合成工艺及工艺路线。选择分子量1000的烯酐及新戊基多元醇为原料，选用两种催化剂，一种是磷酸酯，另一种是碱性金属盐类，并对反应条件进行了考察，确定适宜的反应时间是10～12 h，温度为170～180，适宜的原料配比为1∶1.2，较好的真空度为0.08 MPa，并运用红外光谱对添加剂进行了结构表征。

烯酐;新戊基多元醇;分散剂

Abstract:Taking polyisobutenyl succinic anhydride of number average molecular weight of about 1000 and neopentyl polyol as raw materials，succinate ashless dispersant was synthesized through esterification reaction and the reaction conditions were discussed.Phosphate and basic metal salts were selected as catalysts in the esterification reaction and the appropriate esterification conditions were obtained as follows:the reaction time is 10～12 h，the reaction temperature is 170～180，the ratio of monomers is 1∶1.2 and the vacuum degree is 0.08 MPa.The additive structures were characterized by IR spectrum.

Key words:polyisobutenyl succinic anhydride;neopentyl polyol;dispersant

0 引言

在内燃机运转过程中，可能形成许多漆膜、油泥和积炭，造成油路和滤网的堵塞，活塞的磨损，活塞环粘结，而且由于油泥中含有许多水分，使内燃机很容易被锈蚀，缩短了内燃机的使用寿命。为解决上述问题，人们广泛采用在润滑油中加入分散剂的方法，分散剂的作用是将油泥、漆膜和积炭的前体分散在油中，阻止其形成油泥、漆膜和积炭，延长换油期，从而延长内燃机的使用寿命［1］。

现代内燃机油添加剂配方中主要以丁二酰亚胺型无灰分散剂为主，其使用量占分散剂总量的80%以上。其化学结构由亲油基、极性基和连接部分组成，该结构在润滑油中极易形成胶团，保证了它对液态的初期氧化产物具有极强的增溶作用，以及对积炭、烟灰等固态微粒具有很好的胶溶分散作用［2］。同时，无灰分散剂还能够中和燃烧所生成的酸［3］。……